This document specifies the method for non-destructive thickness measurement via the magnetic type of electrodeposited nickel coatings, also called “e-nickel”, on magnetic or non-magnetic substrates.
It can be that the method is not applicable to autocatalytic (electroless) nickel coatings depending on their chemical composition since this coating is often non-magnetic.
For the purposes of this document, two types of substrates are distinguished:
a) nickel coatings on magnetic substrates (type A coatings).
b) nickel coatings on non-magnetic substrates (type B coatings).
Not all instruments are applicable to both types of coating.
The effective measuring ranges of instruments using the principle of magnetic attraction are up to 50 µm for type A coatings, and up to 25 µm for type B coatings.
For instruments using the principle of reluctance, the effective ranges are much greater, up to 1 mm or even more. This method is applicable for both types of coatings.
Required form fields are indicated by an asterisk (*) character.
You are now following this standard. Weekly digest emails will be sent to update you on the following activities:
You can manage your follow preferences from your Account. Please check your mailbox junk folder if you don't receive the weekly email.
You have successfully unsubscribed from weekly updates for this standard.
Comment by: