Find out what cookies we use and how to disable themThis document specifies a method of measuring the case hardening depth, surface hardening depth, nitriding hardness depth and total thickness of surface hardening depth obtained, e.g. thermal (flame and induction hardening, electron beam hardening, laser beam hardening, etc.) or thermochemical (carbonitriding, carburizing and hardening, hardening and nitriding, etc.) treatment.